Medium-low temperature Accelerator
Medium-low temperature Accelerator XBA-402S
Introduction
XBA-402S is an accelerator and benefited to cement strength development
XBA-402S can effectively shorten the thickening time of cement slurry.
XBA-402S can increase set cement’s early strength and shorten WOC(wait of cement) effectively.
XBA-402S could be used through wet or dry mixing.
Basic performance
Product |
Appearance |
Dosage(BWOC) |
XBA-402S |
Gray or off-white powder |
2~6% |
Slurry performance
Item |
Experimental condition |
Technical indicator |
|
Initial consistency, Bc |
32℃,8.3MPa,17min |
≤30 |
|
Rate of thickening time (Ratio of additive added and non-added) |
≤0.5 |
||
6h compressive strength,MPa |
39℃,0.1MPa |
≥4.0 |
|
Rate of 24h compressive strength (Ratio of additive added and non-added) |
≥1.0 |
||
Slurry composition |
API class G(HSR) 800g,XBA-402S 24g(3%),fresh water,defoamer 1.2g (0.15%). Slurry density: 1.90±0.02g/cm3(adjusted by adding fresh water)。 |
Packaging and Storage
Packaging: XBA-402S is packed with 25kg bag, or according to user requirements.
Storage: The packed products should be saved in a dry and ventilated place, avoid rain, moisture, exposure and heat.